Resini SZUV-T1150-ga otutu resistance
Gbogbogbo Ifihan
Aw?n abuda:
SZUV -T1150 ni a ofeefee SL resini eyi ti o ni unmatched gbona i??. O le withstand aw?n iw?n otutu ni excess ti 200 ℃ ni a kukuru akoko ati 120 ℃ ni igba pip?. O ti wa ni ap?r? fun mimu kan jakejado orisirisi ti ga otutu ati ikolu ti igbeyewo ohun elo.
A?oju Aw?n ?ya ara ?r?
Agbara giga ati Resistance to dara
SZUV-T1150 le duro soke ?riniinitutu, omi ati nkanmimu, g?g? bi aw?n petirolu, gbigbe ito, epo ati coolant. P?lu resistance ooru ti ko ni ibamu, o dara fun sisan, HVAC, ina, ohun elo irin??, mimu ati aw?n ohun elo idanwo oju eefin af?f?.
K? Yiyara ati Dagbasoke yiyara
Nipa ipese i?el?p? iyara ati aw?n ?ya p?lu didan, dada ti o r?run lati mu, SZUV-T1150 le pari i?? akan?e r? lati iyaworan si aw?n apakan idanwo ni akoko kukuru.
Ohun elo A?oju
-Lab?-ni-Hood paati igbeyewo
-High otutu RTV igbáti
- Idanwo oju eefin af?f?
-Im?l? imuduro igbeyewo
-Akop? autoclave tooling
-HVAC paati igbeyewo
-Gbigbemi ?p?l?p? igbeyewo
-Orthodontics
Aw?n ?ran Ohun elo
?k?
?w? Molds
Aw?n ?ya ara ?r? laif?w?yi
Ap?r? apoti
Ap?r? aworan
I?oogun
?
| Ifarahan | funfun |
| iwuwo | 1.13g/cm3@ 25 ℃ |
| Igi iki | 430~510 cps @ 27 ℃ |
| Dp | 0.155 mm |
| Ec | 7,3 mJ / cm2 |
| Building Layer sisanra | 0.05 ~ 0.12mm |
?
| Wiw?n | ?na idanwo | Iye | |
| 90-iseju UV l?hin-ni arowoto | 90-i??ju UV +2 wakati @ 160 ℃ igbona l?hin imularada | ||
| Lile, Shore D | ASTM D2240 | 88 | 92 |
| Modulu Flexural, Mpa | ASTM D790 | 2776-3284 | 3601-3728 |
| Agbara Flexural, Mpa | ASTM D790 | 63-84 | 92-105 |
| Modulu fif?, MPa | ASTM D638 | 2942-3233 | 3581-3878 |
| Agbara fif?, MPa | ASTM D638 | 60-71 | 55-65 |
| Elongation ni isinmi | ASTM D638 | 4-7% | 4-6% |
| Agbara ipa, ogbontarigi lzod, J/m | ASTM D256 | 12-23 | 11-19 |
| Ooru yiy? kuro ni iw?n otutu, ℃ | ASTM D 648 @ 66PSI | 91 | 108 |
| Gilasi iyipada, Tg, ℃ | DMA, ga | 120 | 132 |
| Olus?dipúp? ti imugboroosi gbona, E6/℃ | TMA (T | 78 | 85 |
| Imudara igbona, W/m.℃ | ? | 0.179 | ? |
| iwuwo | ? | 1.26 | ? |
| Gbigba omi | ASTM D 570-98 | 0.48% | 0.45% |
?
?
?
?
?
?
?
?
?
?
?
?
?